GaN is more stable than most metal oxide semiconductors for the photocatalytic degradation of organic pollutants in harsh conditions, while its catalytic efficiency has been difficult to be substantially improved. In this study, the tribocatalytic degradation of organic dyes by GaN nanoparticles has been investigated. Stimulated through magnetic stirring using homemade Teflon magnetic rotary disks in glass beakers, the GaN nanoparticles were found to induce negligible degradation in rhodamine B (RhB) and methyl orange (MO) solutions. Surprisingly, the degradation was greatly enhanced in beakers with Ti and Al 2O 3 coatings on their bottoms: 99.2% and 99.8% of the 20 mg/L RhB solutions were degraded in 3 h for the Ti and Al 2O 3 coatings, respectively, and 56% and 60.2% of the 20 mg/L MO solutions were degraded in 24 h for the Ti and Al 2O 3 coatings, respectively. Moreover, the MO molecules were only broken into smaller organic molecules for the Ti coating, while they were completely degraded for the Al 2O 3 coating. These findings are important for the catalytic degradation of organic pollutants by GaN in harsh environments and for achieving a better understanding of tribocatalysis as well. Abstract GaN is more stable than most metal oxide semiconductors for the photocatalytic degradation of organic pollutants in harsh conditions, while its catalytic efficiency has been difficult to be substantially improved. In this study, the tribocatalytic degradation of organic dyes by GaN nanoparticles has been investigated. Stimulated through magnetic stirring using homemade Teflon magnetic rotary disks in glass beakers, the GaN nanoparticles were found to induce negligible degradation in rhodamine B (RhB) and methyl orange (MO) solutions. Surprisingly, the degradation was greatly enhanced in beakers with Ti and Al 2O 3 coatings on their bottoms: 99.2% and 99.8% of the 20 mg/L RhB solutions were degraded in 3 h for the Ti and Al 2O 3 coatings, respectively, and 56% and 60.2% of the 20 mg/L MO solutions were degraded in 24 h for the Ti and Al 2O 3 coatings, respectively. Moreover, the MO molecules were only broken into smaller organic molecules for the Ti coating, while they were completely degraded for the Al 2O 3 coating. These findings are important for the catalytic degradation of organic pollutants by GaN in harsh environments and for achieving a better understanding of tribocatalysis as well. Keywords: tribocatalysis; coatings; dye degradation; GaN